含未焊透缺陷的高温高压蒸汽管道的安全分析与评估

周 孟，李海明，姚新宽，冯晓亮，徐海亮

（淄博市特种设备检验研究院，山东 淄博  255086）

摘 要：主蒸汽管道作为电站锅炉的主要承压部件，一直处在高温高压的状态下运行。由于安装时焊接工艺控制不严格，造成在定期检验时发现部分焊缝存在未焊透形式的焊接缺陷。对未焊透缺陷最严重的部位，进行了无损检测分析、化学成分分析、金相和硬度分析、安全评定以及剩余寿命的评估，为管道的继续使用提出了合理的建议。

关键词：未焊透；高温高压；蒸汽管道；安全分析；评估

Safety analysis and evaluation of high-temperature and high-pressure steam pipelines with incomplete penetration defects

Zhou Meng, Li Haiming,Yao Xingkuan, Feng Xiaoliang,Xu Hailiang

（Zibo Special Equipment Inspection and Research Institute  Zibo  255086）

Abstract: The main steam pipeline, as the main pressure bearing component of power plant boilers, has been operating under high temperature and pressure. Due to the lack of strict welding process control during installation, some welds were found to have incomplete welding defects during regular inspections. Non destructive testing analysis, chemical composition analysis, metallographic and hardness analysis, safety assessment, and residual life assessment were conducted on the most severe areas of incomplete penetration defects. Finally, reasonable suggestions were proposed for the continued use of the pipeline.

Key words: Incomplete penetration; High temperature and pressure; Steampipes; Safety analysis; Assess.

0 引言

某石化企业2台型号为UG-260/9.81-M电站锅炉主蒸汽管道进行定期检验，锅炉的结构为循环流化床锅炉，额定蒸发量为260t/h，额定压力为9.81MPa,额定温度为540℃。锅炉正式投用大约有8年的时间，主蒸汽管道及母管总长约300米，规格分别为φ273×20mm和φ325×25mm，材质为12Cr1MoVG，运行时间约60000小时。

在对锅炉主汽管道进行射线检测时，发现了20多条焊缝存在未焊透形式的缺陷。未焊透缺陷的存在在管道使用中的会产生很多的危害，主要表现在以下几个方面：一是减少了焊接接头的有效截面积，导致焊接接头强度的下降；二是会造成应力的集中，成为裂纹产生的源头，会严重削弱了焊缝的抗疲劳强度的能力。因此，未焊透缺陷是不允许存在的缺陷类型，发现此类型缺陷应进行消除。由于本次锅炉检修周期非常短，若是采用重新返修焊口的方法消除缺陷，会造成检修时间的增加，不能保证锅炉按计划进行点火，会给企业造成上千万的经济损失。

（周 孟）含未焊透缺陷的在用高温高压蒸汽管道安全分析与寿命评估.pdf